Proflex® Crack Filler
for Asphalt Paving
 |
|
1500 Series |
|
Product Data Sheet |
|
F1509 Black |
|
|
|
This product is a unique, extremely
flexible, two-component epoxy membrane. It is solvent-free
and exhibits excellent tensile strength and elongation under
ambient as well as colder temperatures. |
|
|
|
ADVANTAGES |
|
|
-
100 % solids for low odor during
installation
-
Less hazardous.
-
Self-priming and leveling on properly
prepared surfaces.
-
Self-leveling when sufficient material
is applied.
-
Fills depressions, spalled areas and
cracks.
-
Absorbs movement to help prevent
reflective cracking.
-
Remains flexible over a wide range of
temperatures.
|
|
|
|
SURFACE PREPARATION |
|
Surface and air temperature must be a minimum of 50° F.
during installation and initial cure. Surface should
be checked for soundness. Standard surface preparation
practice should be followed, including thorough cleaning and
drying. |
|
|
|
TYPICAL PROPERTIES (When mixed) |
|
Mix Ratio: |
1:1 by volume |
|
Density: |
9.5 lbs / gal. |
|
Viscosity (Brookfield): |
750 cps |
|
Pot Life: |
45 min. to 1 hr. depending on temperature |
|
Gel Time: |
55 min. |
|
Cure Time: |
24 hours |
|
Shore D Hardness (72 hrs): |
52 |
|
Adhesion (aged): |
100% @ 730 psi |
|
Impact Resistance: |
> 174 inch-lbs. |
|
Mandrel Bend: |
1/8” no crack |
|
Colors: |
Black |
|
|
7 days |
15 days |
|
Tensile Strength – Ambient: |
808 psi |
1390 psi |
|
Tensile Strength – Chilled: |
3900 psi |
6610 psi |
|
Elongation – Ambient: |
139 % |
132 % |
|
Elongation – Chilled: |
68 % |
27 % |
|
Modulus of Elasticity – Ambient: |
79.7 psi |
331 psi |
|
Modulus of Elasticity – Chilled: |
1150 psi |
1180 psi |
|
Hot Tire Print |
No permanent imprint @ 2 hrs., 140°F |
|
|
|
|
|
|
|
|
|
|
|